Aluminium Castings in LM4

Home › Forums › Materials › Aluminium Castings in LM4

Viewing 5 posts - 1 through 5 (of 5 total)
  • Author
    Posts
  • 17 March 2013 at 21:56 #29480
    Alan Worland 1
    Participant
      @alanworland1
      Advert
      17 March 2013 at 21:56 #114649
      Alan Worland 1
      Participant
        @alanworland1

        I have a set of aluminium castings to make the side valve 'Whippet' engine which have been cast in LM4 alloy.

        I am sure these are usable as is, but seem a bit on the 'soft' side and I was hoping to harden them up in some (easy) way

        Has anyone used this quite common casting alloy and done any heat treatment to it?

        Alan

        18 March 2013 at 11:06 #114679
        Ian S C
        Participant
          @iansc

          There is quite a bit on google. The heat treatment gives you LM-4 TF, it consists of;

          Solution treatment, 6 to 16hrs at 505 to 520*C followed by quenching in hot water.

          Precipitation treatment, 6 to 18hrs at 160*C then allow to cool in air.

          I'm not that sure if there would be a great advantage, but you would have to study the information, I don't think it makes much difference to the hardness of the metal, it proberbly improves the grain structure of the metal. Ian S C

          18 March 2013 at 11:54 #114681
          Roderick Jenkins
          Participant
            @roderickjenkins93242

            The copper content of LM4 allows it to precipitation harden. The copper precipitates inhibit the movement of dislocations which means that the metal will be harder and tougher. If you have equipment that will allow you to closely follow the recipe that Ian has given I'm sure that would be beneficial, otherwise I would recommend leaving it in the as cast state. Some natural age hardening is likely to occur over time anyway.

            Rod

            18 March 2013 at 23:43 #114723
            Alan Worland 1
            Participant
              @alanworland1

              Thanks guys, I did do an internet search and found what you have, I was after something simple! as I dont have the facilities to carry out this process.

              I shall use them as is and go carefull with the machining to avoid pickup and possible problems with tapped holes.

              Alan

            • Author
              Posts
            Viewing 5 posts - 1 through 5 (of 5 total)
            • Please log in to reply to this topic. Registering is free and easy using the links on the menu at the top of this page.

            Latest Replies
            Report Bug
            Code of Conduct
            Help & FAQs
            Advert

            Latest Replies

            Home › Forums › Materials › Topics

            Viewing 25 topics - 1 through 25 (of 25 total)
            Viewing 25 topics - 1 through 25 (of 25 total)

            View full reply list.

            Advert

            Latest Issues

            Subscribe
            Buy Latest/Back Issues

            Newsletter Sign-up

            Latest Replies